POLYLACK F is made on the basis of flame retardants, carbon and gas forming additives and an aqueous dispersion of synthetic resin. The surface painted with an intumescent paint is protected during a fire and prevents the flame from spreading due to the formation of a foamy carbon layer on the thermal insulation surface that stops the burning of the polymer insulating coating at an early stage.
Intumescent paint is intended for sealing:
Technical Approval ITB No. AT-15-8457 / 2010, AT-15-8476 / 2010
Certificate of compliance ITB-1991 / W, ITB-1989 / W
color | white |
density | 1,33 ± 5% g/cm3 |
time of shell formation | 120 min |
complete drying | 24 h |
temperature resistance | -40 st. C to +120 st. C |
swell | ≥25 |
dry film thickness | min. 0,5 mm |
storage temperature | +5 st. C to +25 st. C |
storage period | 12 months |